405 BA finish high quality stainless steel strip manufacture, 405 stainless steel round bar

ASTM A268 ASME SA268 S40500 405 Stainless Steel 1.4002 is a 12% chromium steel, designed to be used in the as welded condition.  Unlike other grades in the 12% chromium category, 405 is not susceptible to extensive hardening through air cooling from high temperature. Commonly used for annealing boxes, steam nozzles, quenching racks, partitions and other fabrications that cannot be annealed after welded. Soft and ductile, 405 can be easily machined using most standard practices. Experienced machinists comment that 405 machines similarly to 4130 alloy steel. 405 can be easily spun, drawn and formed using common forming procedures.
send email to us

Products Details

C Mn Si P S Cr
Min           11.5
Max 0.15 0.50 1.00 0.04 0.03 13.5
Al C Mn P S Cr Si Ni N Cu
0.10-0.30 max. 0.08 max. 1.00 max. 0.040 max. 0,030 11.5 – 14.5 max 1.00 max, 0.5 – –
Condition Tensile Strength, PSi Yield Strength 0.2% PSi Elongation % Reduction of are % Hardness HB
A 115,000       241
HT 120,000 90,000 12 40 269
Commonly used for annealing boxes, steam nozzles, quenching racks, partitions and other fabrications that cannot be annealed after welding.
405 stainless steel plate sizes and specifications
Grade 405
Cold rolled stainless steel plate Thickness: 0.3mm- 16.0mm, Width: 1000mm - 2000mm, Length: as requirements, Surface: 2B/BA/SB/8K/HL/1D/2D etc
Hot rolled stainless steel sheet Thickness: 3.0mm - 300mm, Width: 1000mm - 3000mm Length: as requirements, Surface: No.1/pickling
  Standard ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303, BS 1449, DN17441, G4305
Stainless steel plate Thickness: 8.0mm - 300mm, Width: 1000mm - 3000mm Length: as requirements, Surface: No.1/pickling
405 stainless steel strip sizes and specifications
Grade 405
Cold rolled stainless steel strip Thickness: 0.3mm- 3.0mm, Width: 5mm - 900mm, Surface: 2B/BA/SB/8K/HL/1D/2D etc
Hot rolled stainless steel strip Thickness: 3.0mm - 16mm, Width: 10mm - 900mm Surface: No.1/pickling
Stainless steel foil Thickness: 0.02mm- 0.2mm, Width: Less than 600mm, Surface: 2B
  Standard ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303,  BS 1449, DN17441, G4305
 
405 stainless steel coil sizes and specifications
Grade 405
Cold rolled stainless steel coil Thickness: 0.3mm- 3.0mm, Width: 1000mm - 2000mm, Surface: 2B/BA/SB/8K/HL/1D/2D etc
Hot rolled stainless steel coil Thickness: 3.0mm - 16mm, Width: 1000mm - 2000mm Surface: No.1/pickling
  Standard ASTM A240/A480, ASTM B688, ASTM B463/SB463, ASTM B168/SB168, ASTM B443/SB443/B424/SB424B625/SB625 B575/SB575, JIS G4303,   BS 1449, DN17441, G4305
 
405 stainless steel pipe sizes and specifications
Grade 405
Stainless steel seamless pipe Outside diameter: 4.0 - 1219mm, Thickness: 0.5 -100mm, Length: 24000mm
Stainless steel welded pipe Outside diameter: 6.0 - 2800mm, Thickness: 0.3 -45mm,Length: 18000mm
Stainless steel capillary pipe Outside diameter: 0.4 - 16.0mm, Thickness: 0.1 -2.0mm, Length: 18000mm
Stainless steel welded sanitary pipe Outside diameter:8.0- 850mm, Thickness: 1.0 -6.0mm
Stainless steel seamless sanitary pipe Outside diameter: 6.0- 219mm, Thickness: 1.0 -6.0mm
Stainless steel square pipe Side Length: 4*4 - 300*300mm, Thickness: 0.25 - 8.0mm, Length: 18000mm
Stainless steel rectangular pipe Side Length: 4*6 - 200*400mm, Thickness: 0.25 - 8.0mm, Length: 18000mm
Stainless steel coil pipe Outside diameter: 0.4 - 16mm, Thickness: 0.1 - 2.11mm
  Standard American Standard: ASTM A312, ASME SA269, ASTM A269, ASME SA213, ASTM A213 ASTM A511 ASTM A789, ASTM A790, ASTM A376, ASME SA335, B161, SB163, SB338, SB667/668 Germany Standard: DIN2462.1-1981, DIN17456-85, DIN17458-85· European Standard: EN10216-5, EN10216-2 Japanese Standard: JIS G3463-2006, JISG3459-2012 Russian Standard: GOST 9941-81
405 stainless steel profile sizes and specifications
Grade 405
Specification EN, DIN, JIS, ASTM, BS, ASME, AISI, ISO
Standard ASTM A276/ASME SA276, ASTM A479/ASME SA479 & ASTM A164/ASME SA164 .
Stainless steel round Bar Diameter: 2mm - 600mm
Stainless steel bright Bar Diameter: 2mm - 600mm
Stainless steel hex Bar Dimension: 6mm - 80mm
Stainless steel square bar Dimension: 3.0 - 180mm  
Stainless steel flat bar Thickness: 0.5mm - 200mm, Width: 1.5mm - 250 mm
Stainless steel angle bar as requirements
Length Normally 6m, or produce as requirements
Surface Black, Bright. Peeled and Polished, Solution annealed.
Delivery condition cold drawn, hot rolled, forged, grinding, centerless grinding
Tolerance H8, H9, H10, H11, H12, H13,K9, K10, K11, K12 or as per clients’ requirements
Soft and ductile, 405 can be easily machined using most standard practices. Experienced machinists comment that 405 machines similarly to 4130 alloy steel.405 can be easily spun, drawn and formed using common forming procedures.
Al C Mn P S Cr Si Ni N Cu
0.10-0.30 max. 0.08 max. 1.00 max. 0.040 max. 0.030 11.5 – 14.5 max 1.00 max 0.60 – –
Al C Mn P S Cr Si Ni N Cu
0.10-0.30 max. 0.08 max. 1.00 max. 0.040 max. 0.015 12.0 – 14.0 max 1.00 max 0.60 – –
Material Grade Material Number Tensile StrengthRmN/mm² ksi(MPa) min Yield StrengthRp0.2%N/mm²(MPa) min Elongation(%) BrinellHardness Testmax RockwellHardness Testmax
TP405 S40500 60 (415) 30 (205) 20 207 95
Material Grade Material Number Tensile Strength Rm N/mm² ksi(MPa) min Yield Strength Rp0.2% N/mm²(MPa) min Elongation (%)
TP 405 1.4002 400-600 230 17
Commonly used for annealing boxes, steam nozzles, quenching racks, partitions and other fabrications that cannot be annealed after welding.Soft and ductile, 405 can be easily machined using most standard practices. Experienced machinists comment that 405 machines similarly to 4130 alloy steel.405 can be easily spun, drawn and formed using common forming procedures.405 can be welded using shielded fusion and resistance techniques. Oxyacetylene welding is not recommended. Use 405 Cb electrodes that contain columbium rather than aluminum to control hardening. Post weld annealing will maximize ductility.Soak at 1500-1600°F(817-871°C) and then quickly increase to 1900-2050°F(1038-1121°C). Do not remain at this temperature as the result will be excessive grain growth. Do not work below 1500°F(816 °C). After forging, air cool and anneal.Soak at 1200-1400°F(649-760°C), air cool.While this alloy does not respond appreciably to heat treatment, soaking at 1800-1850°F(982-1010°C) followed by oil quenching will increase mechanical properties.

Previous:ASTM B168 Cold Rolled Inconel 600 Alloy Plate in Stock,Inconel 600 bar Suppliers,manfacture Inconel 600 Strip

Next:Rene 41 nickel wire rod, Rene 41 round bar, Rene 41 plate, Rene 41 sheet, Rene 41 strip

Titanium metal foil, Stainless Steel Welded Pipe, Asme B36 19, 718 Alloy, Tisco stainless steel plate, Stainless Diamond Plate, 321 Stainless Steel Sheet, Stainless Steel Mirror Sheet, Stainless Steel Corrugated Sheet, Stainless Steel Strips,

Featured Products

Contact us

Please feel free to give your inquiry in the form below We will reply you in 24 hours